Effect of microstructure on the fracture response of advanced high strength steels
MetadataShow full item record
The effect of constituent hardness on formability performance for higher-strength dual phase (DP) steels was evaluated. A commercially-produced DP steel with 1080 MPa ultimate tensile strength (UTS) was processed to create eight additional constituent hardness conditions by tempering and cold-rolling, processes that primarily affected constituent hardness properties. Using nanoindentation, ferrite and martensite hardness values for the nine conditions of the DP steel (as-received, four as-tempered, four temper cold-rolled) provided a range of hardness values to evaluate formability performance. ...